API-571 Exam Dumps - Corrosion and Materials Professional

API RP 571 under Thermal Fatigue highlights:

“Differential thermal expansion between dissimilar materials (e.g., carbon steel and stainless steel) in welds causes high cyclic stresses that can result in thermal fatigue cracking.”

“These stresses typically occur during transient thermal cycling such as startup/shutdown operations.”

(Reference: API RP 571, Section 4.2.1.5 – Thermal Fatigue)

Thus, the correct mechanism resulting from differential expansion in bimetallic welds is thermal fatigue, making option B correct.

API RP 571 discusses Hydrogen-Induced Cracking (HIC) and Blistering:

“Postweld heat treatment (PWHT) does not significantly reduce susceptibility to HIC, as the mechanism is primarily driven by hydrogen charging in wet H₂S environments and steel cleanliness, not residual stresses.”

“PWHT is more effective for SSC, SOHIC, and other stress-driven mechanisms.”

Thus, HIC will not benefit much from PWHT, making option C correct.

In API RP 571, Carbonate SCC and Alkaline SCC are both discussed under mechanisms that occur in basic (high pH) environments, often with similar contributing conditions and prevention methods. The document highlights:

“Carbonate SCC is considered a subcategory of alkaline stress corrosion cracking. It results from the concentration of alkaline carbonates under thermal insulation or deposits.”

“Both mechanisms involve the same key parameters: elevated temperatures, tensile stress, and high pH solutions.”

(Reference: API RP 571, 3rd Edition, Section 4.2.2.4 and 4.2.2.3)

Because these mechanisms share similar material susceptibility and operating conditions, they are indeed closely related—option B is therefore the accurate and supported answer.

According to API RP 571, in the section on "Chloride Stress Corrosion Cracking (Cl-SCC)", several critical factors are outlined that contribute to the initiation and propagation of this mechanism. The document states:

“Critical factors include the presence of chlorides (even at ppm levels), oxygen, elevated temperatures, tensile stress, and susceptible materials such as austenitic stainless steels and some nickel alloys.”

“Oxygen is an accelerant and promotes pitting that can lead to SCC initiation.”

(Reference: API RP 571, 3rd Edition, Section 4.2.2.2)

Therefore, the presence of oxygen is a well-documented critical factor in Cl-SCC. It acts in conjunction with chlorides to initiate localized pitting, which then progresses into cracking. Hence, option B is the correct choice.